盐酸-硫酸法定量分析棉/聚酯纤维/氨纶混纺织物的研究

doi:10.19398/j.att.202103015

摘要/Abstract

摘要：

为了优化定量分析棉/聚酯纤维/氨纶混纺织物的方法,根据新发布的国标GB/T 38015-2019《纺织品定量化学分析氨纶与某些其他纤维的混合物》设计了盐酸-硫酸法:采用20% HCl在70 ℃,30 min条件下溶解棉,然后用75% H₂SO₄在50 ℃,1 h条件下溶解氨纶,根据质量损失,求得各组分的质量分数,完成棉/聚酯纤维/氨纶混纺织物的定量分析。采用盐酸-硫酸法对10块不同规格的棉/聚酯纤维/氨纶混纺织物进行定量分析,并与传统的拆分-75% H₂SO₄法及DMF-75% H₂SO₄法进行分析比较。结果表明:20% HCl(70 ℃,30 min)中聚酯纤维的质量修正系数为1.00,新设计的盐酸-硫酸法切实可行,并具有操作方便、数据准确等优点。

关键词: 棉, 聚酯纤维, 氨纶, 混纺织物, 定量分析

Abstract:

In order to optimize the method of quantitative analysis of cotton/polyester fiber/spandex blend fabric, a hydrochloric acid-sulfuric acid process was designed according to newly issued national standard Textiles-Quantitative Chemical Analysis-Mixtures of Elastane and Some Other Fibers (GB/T 38015—2019): 20% HCl was used to dissolve cotton at 70℃ for 30 min, and then 75% H₂SO₄ was adopted to dissolve spandex at 50 ℃ for 1 h. Next, the mass fraction of each component was obtained according to the mass loss, thus the quantitative analysis of cotton/polyester fiber/spandex blend fabric was completed. In this paper, 10 different specifications of cotton/polyester fiber/spandex blend fabric were quantitatively analyzed through hydrochloric acid-sulfuric acid process, and then compared with the traditional split-75% H₂SO₄ method and DMF-75% H₂SO₄ method. The results revealed that the quality correction coefficient of polyester fiber in 20% HCl (70 ℃, 30 min)was 1.00, and the newly designed hydrochloric acid-sulfuric acid process was proved to be feasible, with the advantages of easy operation and accurate data.

Key words: cotton, polyester fiber, spandex, blend fabric, quantitative analysis

中图分类号:

TS106.8

张弘康, 张芸娟, 周兆懿. 盐酸-硫酸法定量分析棉/聚酯纤维/氨纶混纺织物的研究[J]. 现代纺织技术, 2022, 30(2): 63-67.

ZHANG Hongkang, ZHANG Yunjuan, ZHOU Zhaoyi. A quantitative analysis of cotton/polyester/spandex composite fabricthrough hydrochloric acid-sulfuric acid process[J]. Advanced Textile Technology, 2022, 30(2): 63-67.

图/表 4

参考文献 12

[1]	许艳, 周衡书, 徐国强, 等. 棉、黏胶、氨纶弹力织物成分含量测试方法探讨[J]. 天津纺织科技, 2020(6):40-42.
	XU Yan, ZHOU Hengshu, XU Guoqiang, et al. Discussion on the quantitative analysis method of cotton, viscose fiber and spandex[J]. Tianjin Textile Science & Technology, 2020(6):40-42.
[2]	白玉林, 何凤. 氨纶弹力织物产品开发与设计[J]. 上海纺织科技, 2005, 33(3):42-44.
	BAI Yulin, HE Feng. Development and design of spandex fabric[J]. Shanghai Textile Science & Technology, 2005, 33(3):42-44.
[3]	田娜娜, 刘艳君. 双组分氨纶混纺面料中纤维含量的定量分析方法[J]. 合成纤维, 2015, 44(5):51-52.
	TIAN Nana, LIU Yanjun. The quantitative chemical analysis methods of two component spandex blend fabric[J]. Synthetic Fiber in China, 2015, 44(5):51-52.
[4]	张玲香. 棉锦涤氨纶弹力提花交织物的染整工艺[J]. 印染, 2006, 32(3):9-12.
	ZHANG Lingxiang. Dyeing and finishing of cotton/polyamide/polyester/polyurethane jacquard mixture[J]. China Dyeing & Finishing, 2006, 32(3):9-12.
[5]	李晓菲. 氨纶/纤维素纤维混纺产品定量方法对比[J]. 中国纤检, 2020(9):69-71.
	LI Xiaofei. The comparison of quantitative methods for spandex and cellulose blended products[J]. China Fiber Inspection, 2020(9):69-71.
[6]	王超, 李俊杏, 马兵联, 等. 纬编涤棉氨弹性绒类织物染整工艺实践[J]. 针织工业, 2009(1):50-52.
	WANG Chao, LI Junxing, MA Binglian, et al. A practice of dyeing and finishing technologyof the weft knitted polyester/cotton/polyurethane elastic fabric[J]. Knitting Industries, 2009(1):50-52.
[7]	孙锋, 张晓红. 涤棉双面针织物透湿等性能分析[J]. 五邑大学学报(自然科学版), 1995, 9(3):39-44.
	SUN Feng, ZHANG Xiaohong. The analysis of the dia-moisture etc. properties for the double jersey of polyester and cotton[J]. Journal of Wuyi University(Natural Science Edition), 1995, 9(3):39-44.
[8]	王超, 闫利民, 李俊杏. 棉盖涤氨纶针织物染整工艺[J]. 印染, 2008, 34(12):18-20.
	WANG Chao, YAN Limin, LI Junxing. Wet processing of cotton and polyester double-faced knitgoods containing polyurethane[J]. China Dyeing & Finishing, 2008, 34(12):18-20.
[9]	王京力, 赵珍玉, 孙克强, 等. 基于近红外光谱法检测棉/聚酯/氨纶织物的纤维含量[J]. 上海纺织科技, 2020, 48(4):51-53.
	WANG Jingli, ZHAO Zhenyu, SUN Keqiang, et al. Detection of fiber content in cotton polyester spandex three component fabric based on near infrared spectroscopy[J]. Shanghai Textile Science & Technology, 2020, 48(4):51-53.
[10]	李昱芃, 甘亚雯. 对牛仔面料棉/聚酯/氨纶三组分纤维含量检测方法的探讨[J]. 中国纤检, 2011(18):62-64.
	LI Yupeng, GAN Yawen. Discussion on the test method of cotton/polyester/elastane fiber content[J]. China Fiber Inspection, 2011(18):62-64.
[11]	潘其胜. 二甲基甲酰胺致职业性慢性中毒性肝病1例分析[J]. 海峡预防医学杂志, 2021, 27(1):52-54.
	PAN Qisheng. A case study of occupational chronic toxic hepatic disease caused by N, N-dimethylfor-mamide[J]. Strait Journal of Preventive Medicine, 2021, 27(1):52-54.
[12]	张丽丽, 于洋, 牛文凤, 等. 高产量化学品N,N-二甲基甲酰胺的生态环境风险与管控措施[J]. 生态毒理学报, 2020, 15(5):59-68.
	ZHANG Lili, YU Yang, NIU Wenfeng, et al. Ecological risk and management measures of high yield chemical N,N-dimethylformamide[J]. Asian Journal of Ecotoxicology, 2020, 15(5):59-68.

100%聚酯纤维织物	平方米质量/(g·m^-2)	棉/聚酯纤维/氨纶混纺织物	平方米质量/(g·m^-2)	氨纶线密度/dtex
白色机织物	83.5	白色机织物	181.2	77.8
红色机织物	103.4	红色机织物	162.6	14.6
棕色机织物	138.0	黑色机织物	109.2	44.4
绿色机织物	80.1	红黑夹色机织物	327.7	71.1
黑色机织物	59.3	牛仔机织物	288.9	8.0
黑色针织物	95.9	黑色针织物	273.1	16.7
黑白夹色针织物	111.6	灰色针织物	264.4	33.3
白色针织物	281.8	蓝色针织物	243.5	22.2
藏青色针织物	323.4	藏青色针织物	268.4	40.0
粉色针织物	117.2	牛仔针织物	281.7	11.9

100%聚酯纤维织物	平方米质量/(g·m^-2)	棉/聚酯纤维/氨纶混纺织物	平方米质量/(g·m^-2)	氨纶线密度/dtex
白色机织物	83.5	白色机织物	181.2	77.8
红色机织物	103.4	红色机织物	162.6	14.6
棕色机织物	138.0	黑色机织物	109.2	44.4
绿色机织物	80.1	红黑夹色机织物	327.7	71.1
黑色机织物	59.3	牛仔机织物	288.9	8.0
黑色针织物	95.9	黑色针织物	273.1	16.7
黑白夹色针织物	111.6	灰色针织物	264.4	33.3
白色针织物	281.8	蓝色针织物	243.5	22.2
藏青色针织物	323.4	藏青色针织物	268.4	40.0
粉色针织物	117.2	牛仔针织物	281.7	11.9

样品	净干含量
白色机织物	棉:55.3%、聚酯纤维:39.1%、氨纶:5.6%
红色机织物	棉:33.0%、聚酯纤维:63.5%、氨纶:3.5%
黑色机织物	棉:21.6%、聚酯纤维:73.2%、氨纶:5.2%
红黑夹色机织物	棉:21.5%、聚酯纤维:75.5%、氨纶:3.0%
牛仔机织物	棉:61.0%、聚酯纤维:36.5%、氨纶:2.5%
黑色针织物	棉:34.5%、聚酯纤维:63.0%、氨纶:2.5%
灰色针织物	棉:13.5%、聚酯纤维:83.9%、氨纶:2.6%
蓝色针织物	棉:57.7%、聚酯纤维:38.3%、氨纶:4.0%
藏青色针织物	棉:62.5%、聚酯纤维:33.4%、氨纶:4.1%
牛仔针织物	棉:45.8%、聚酯纤维:43.9%、氨纶:10.3%

样品	净干含量
白色机织物	棉:55.3%、聚酯纤维:39.1%、氨纶:5.6%
红色机织物	棉:33.0%、聚酯纤维:63.5%、氨纶:3.5%
黑色机织物	棉:21.6%、聚酯纤维:73.2%、氨纶:5.2%
红黑夹色机织物	棉:21.5%、聚酯纤维:75.5%、氨纶:3.0%
牛仔机织物	棉:61.0%、聚酯纤维:36.5%、氨纶:2.5%
黑色针织物	棉:34.5%、聚酯纤维:63.0%、氨纶:2.5%
灰色针织物	棉:13.5%、聚酯纤维:83.9%、氨纶:2.6%
蓝色针织物	棉:57.7%、聚酯纤维:38.3%、氨纶:4.0%
藏青色针织物	棉:62.5%、聚酯纤维:33.4%、氨纶:4.1%
牛仔针织物	棉:45.8%、聚酯纤维:43.9%、氨纶:10.3%

样品	溶解前净重/g	溶解后净重/g	d值	平均d值
白色机织物	1.0134	1.0121	1.0013	1.0029
红色机织物	1.0556	1.0542	1.0013
棕色机织物	1.0738	1.0714	1.0022
绿色机织物	1.0281	1.0269	1.0012
黑色机织物	1.0397	1.0357	1.0039
黑色针织物	1.1040	1.0962	1.0071
黑白夹色针织物	1.1179	1.1151	1.0025
白色针织物	1.0865	1.0833	1.0030
藏青色针织物	1.0410	1.0366	1.0042
粉色针织物	1.0622	1.0595	1.0025