扩链时间对聚氨酯及其静电纺纳米纤维性能的影响

doi:10.19398/j.att.202202029

现代纺织技术 ›› 2022, Vol. 30 ›› Issue (5): 67-73.DOI: 10.19398/j.att.202202029

扩链时间对聚氨酯及其静电纺纳米纤维性能的影响

王慧佳^a, 陈强^a, 易雨青^a, 施静雅^a, 李妮^a,b

浙江理工大学, a.纺织科学与工程学院;b.先进纺织材料与制备技术教育部重点实验室,杭州 310018

收稿日期:2022-02-22 出版日期:2022-09-10 网络出版日期:2022-09-19
通讯作者:李妮,E-mail:lini@zstu.edu.cn
作者简介:王慧佳(1996-),女,河南驻马店人,硕士研究生,主要从事防水透湿纳米纤维膜方面的研究。
基金资助:
浙江省自然科学基金项目(LY16E030007)

Effect of chain extension time on properties of polyurethane and electrospun nanofibers

WANG Huijia^a, CHEN Qiang^a, YI Yuqing^a, SHI Jingya^a, LI Ni^a,b

a. College of Textile Science and Engineering;b. Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China

Received:2022-02-22 Published:2022-09-10 Online:2022-09-19

摘要/Abstract

摘要： 为了优化聚氨酯纳米纤维膜的力学性能和润湿性能,以聚四氢呋喃醚二醇(PTMG)、4,4′-亚甲基双(苯基异氰酸酯)(4,4′-MDI)和1,4-丁二醇(BDO)为主要原料合成聚氨酯(PU),并利用静电纺丝技术制备PU纳米纤维膜。研究了不同扩链段反应时间对合成聚氨酯物理性质和静电纺纳米纤维膜性能等的影响。采用红外光谱仪(FTIR)、高效液相色谱仪(GPC)、热重分析仪(TG)、扫描电子显微镜(SEM)、多功能拉伸仪和动态/静态接触角仪对PU结构和纤维膜的形貌性能进行表征。结果表明:当扩链反应时间由90 min增加至120 min时,聚氨酯分子量增加,合成聚氨酯的热稳定性略有提高,纳米纤维的成膜性能增强。当扩链反应时间为120 min时,纳米纤维膜的断裂应力为6.8 MPa,断裂伸长率达到139%;疏水性能随着扩链反应时间的增加明显提高,当扩链反应时间为120 min时,240 s后水接触角仍然高达112°。

关键词: 聚氨酯, 扩链时间, 静电纺丝, 力学性能, 耐水性

Abstract: In order to optimize the mechanical properties and wettability of polyurethane nanofiber microporous membrane, polyurethane (PU) was synthetised with polytetrahydrofuran ether glycol (PTMG), 4,4′-methylene bis (phenyl isocyanate)(4,4′-MDI) and 1,4-butanediol (BDO) as the main raw materials. Then nanofiber membranes were prepared by electrospinning. The effects of different chain extension reaction times on the physical properties and fiber membrane properties of synthetic polyurethane were studied. The structure and morphology of PU were characterized by infrared spectrometer (FTIR), gel permeation chromatography (GPC), thermogravimetric analyzer (TG), scanning electron microscope (SEM) and dynamic/static contact angle analyzer. The results showed that the thermal stability of the synthesized polyurethane slightly increased and the film forming performance of the nanofibers increased with the increase of the molecular weight of the polyurethane when the chain expanding reaction time increased from 90 min to 120 min. When the chain extension reaction time was 120 min, the breaking stress of the fiber membrane was 6.8 MPa, and the elongation at break reached the value of 139%. The hydrophobic property was obviously improved with the increase of chain extension reaction time. When the time was 120 min, the water contact angle was still as high as 112° after 240 s.

Key words: polyurethane, chain extension time, electrospinning, mechanical property, water resistance

中图分类号:

TS156

王慧佳, 陈强, 易雨青, 施静雅, 李妮. 扩链时间对聚氨酯及其静电纺纳米纤维性能的影响[J]. 现代纺织技术, 2022, 30(5): 67-73.

WANG Huijia, CHEN Qiang, YI Yuqing, SHI Jingya, LI Ni. Effect of chain extension time on properties of polyurethane and electrospun nanofibers[J]. Advanced Textile Technology, 2022, 30(5): 67-73.

参考文献

[1] SU Y M, WANG T, DING Y L, et al. Preparation technology of solvent-free polyurethane: A mini-review[J]. Chinese Journal of Structural Chemistry 2020, 39(12): 2057-2067.
[2] PENG X M, WANG W S, MA N Y, et al. Research on the post-chain extension of aqueous polyurethane dispersions[J]. RSC Advances, 2016, 6(43): 36510-36515.
[3] 荆晓东,柴可军,赵冠宇.不同芳香二胺扩链剂对聚氨酯弹性体工艺和性能的影响[J].聚氨酯工业,2020,35(6):48-50.
JING Xiaodong, CHAI Kejun, ZHAO Guanyu. Effects of different aromatic diamine chain extenders on the process and properties of polyurethane elastomer[J]. Polyurethane Industry, 2020, 35(6): 48-50.
[4] HU L Q, PU Z J, ZHONG Y Q, et al. Effect of different carboxylic acid group contents on microstructure and properties of waterborne polyurethane dispersions[J]. Journal of Polymer Research, 2020, 27(5): 1022-1030.
[5] ZAMANI E, SHAKI H, RAFIZADEH M, et al. Synthesis and characterization of novel self-colored PET (polyethylene terephthalate) by step-growth polymerization containing dye based on 1,8-naphthalimide group[J]. Fibers and Polymers, 2017, 18(8): 1431-1437.
[6] 高思凡,邱藤,梁日慧,等.芳胺改性水性聚氨酯分散体的合成及性能研究[J].化工新型材料,2022,50(6):185-187.
GAO Sifan, QIU Teng, LIANG Rihui, et al. Synthesis andproperties of aromatic amine-modified waterborne polyurethane dispersion[J]. New Chemical Materials,2022,50(6):185-187.
[7] 刘晓文,化雪晴,刘锦春.聚醚型聚氨酯弹性体玻璃化温度的影响因素[J].热固性树脂,2018,33(3):22-25.
LIU Xiaowen, HUA Xueqing, LIU Jinchun. Factors influencing the glass transition temperature of polyether polyurethane elastomer[J]. Thermoset Polymer, 2018, 33(3): 22-25.
[8] 李亚萍,隋智慧,郭制安,等.有机氟硅改性水性聚氨酯的合成及应用[J].热固性树脂,2021,36(4):15-19.
LI Yaping, SUI Zhihui, GUO Zhi'an, et al. Synthesis and application of organic fluorine-silicon modified waterborne polyurethane[J]. Thermoset Polymer, 2021, 36(4): 15-19.
[9] KIM E Y, LEE J H, LEE D J, et al. Synthesis and properties of highly hydrophilic waterborne polyurethane-ureas containing various hardener content for waterproof breathable fabrics[J]. Journal of Applied Polymer Science, 2013, 129(4): 1745-1751.
[10] WANG J Q, LI Y, TIAN H Y, et al. Waterproof and breathable membranes of waterborne fluorinated polyurethane modified electrospun polyacrylonitrile fibers[J]. Rsc Advances, 2014, 4(105): 61068-61076.
[11] BERGAMASCO S, TAMANTINI S, ZIKELI F, et al. Synthesis and characterizations of eco-friendly organosoly lignin-based polyurethance coating films for the coating industury[J]. Polymers, 2022, 14(3): 416.
[12] GONZALEZ E, FREY M W. Synthesis, characterization and electrospinning of poly(vinyl caprolactam-co-hydroxymethyl acrylamide) to create stimuli-responsive nanofibers[J]. Polymer, 2017, 108: 154-162.
[13] MOU J, WANG X, YU D, et al. Practical two-step chain extension method to prepare sulfonated waterborne polyurethanes based on aliphatic diamine sulphonate[J]. Journal of Applied Polymer Science, 2021, 138(18): 50353.
[14] MAIUOLO L, OLIVITO F, ALGIERI V, et al. Synthesis, characterization and mechanical properties of novel bio-based polyurethane foams using cellulose-derived polyol for chain extension and cellulose citrate as a thickener additive[J]. Polymers 2021, 13(16): 2802.
[15] 叶纯麟,辛忠,梁鹏,等.超高分子量聚乙烯分子量及分子量分布的测定[J].化学反应工程与工艺,2019,35(6):529-533,551.
YE Chunlin, XIN Zhong, LIANG Peng, et al. Determination ofmolecular weight and molecular weight distribution for ultrahigh molecular weight polyethylene[J]. Chemical Reaction Engineering and Technology, 2019, 35(6): 529-533, 551.
[16] QIU Z B, KOMURA M, Ikehara T, et al. Miscibility and crystallization behavior of biodegradable blends of two aliphatic polyesters: Poly(butylene succinate) and poly(ε-caprolactone)[J]. Polymer, 2003, 44(25): 7749-7756.
[17] LIOW K S, SIPAUT C S, MANSA R F, et al. Formulated quasi-solid state electrolyte based on polypyrrole/polyaniline-polyurethane nanocomposite for dye-sensitized solar cell[J]. Journal of Materials Science Materials in Electronics, 2018, 29(14): 11653-11663.

扩链时间对聚氨酯及其静电纺纳米纤维性能的影响

Effect of chain extension time on properties of polyurethane and electrospun nanofibers

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

[1]	杨浩, 田千俊, 石磊, 王淋, 黄志超, 戚栋明. 软段结构对无溶剂聚氨酯树脂微相分离的影响[J]. 现代纺织技术, 2022, 30(5): 74-81.
[2]	聂磊, 李家炜, 严小飞, 戚栋明, 杨晓明, 李耀邦, 朱晨凯. 全降解玻璃纤维增强复合材料的制备及其性能[J]. 现代纺织技术, 2022, 30(5): 104-111.
[3]	李箫, 刘元军, 赵晓明. 静电纺丝纳米纤维基吸声材料的研究进展[J]. 现代纺织技术, 2022, 30(5): 246-258.
[4]	陈志薇, 张顺花. 呋喃基共聚酯PETT纤维的制备及其性能[J]. 现代纺织技术, 2022, 30(4): 102-107.
[5]	石敏, 王騊, 王晟. 快速油-水分离用PVDF/PDMS超疏水膜的一步法制备及性能[J]. 现代纺织技术, 2022, 30(4): 108-114.
[6]	贾子奇, 王琛, 赵甜甜, 刘扬. 氮掺杂氧化石墨烯-TiO₂/ PAN复合纳米纤维膜的制备及其光催化性能[J]. 现代纺织技术, 2022, 30(3): 97-107.
[7]	郑作保, 贾姣, 冯洋洋, 侯一杰, 贾永堂. 静电纺丝制备PMMA/PU新型保暖材料及其性能[J]. 现代纺织技术, 2022, 30(3): 89-96.
[8]	韦悦, 王晟, 纪律律. 硫化镍复合碳纳米纤维的制备及其电催化析氢性能[J]. 现代纺织技术, 2022, 30(3): 81-88.
[9]	宋会芬, 宋丽艳, 潘天浩, 迟长龙, 石素宇, 张学锋. 退火对聚氨酯纤维结构及力学性能的影响[J]. 现代纺织技术, 2022, 30(2): 93-98.
[10]	何文玉, 高雅芳, 张耘箫, 金梦婷, 周岚, 王相林, 刘国金. 纺织基材上P(St-MAA)/WPU复合光子晶体生色结构的快速制备及其性能[J]. 现代纺织技术, 2022, 30(2): 159-168.
[11]	周荣鑫, 葛烨倩. 碳纳米纤维负极材料制备及其电化学性能[J]. 现代纺织技术, 2022, 30(1): 41-46.
[12]	田银彩，林秋虎. 静电纺聚丙烯腈/MgO复合膜的制备及阻燃性能研究[J]. 现代纺织技术, 2021, 0(6): 39-42.
[13]	贾可，刘宁娟，刘玮. 新型碳纳米管膜卷纱的力学及传感性能[J]. 现代纺织技术, 2021, 0(5): 8-12.
[14]	黄益，马军翔，金曦，潘小鹏，郑今欢. 环保型聚氨酯仿皮涂层材料研究进展[J]. 现代纺织技术, 2021, 0(5): 116-128.
[15]	赵甜甜，王琛，冯伟忠，高云莉. 静电纺PAN/TiO₂多孔纳米复合光催化纤维的制备[J]. 现代纺织技术, 2021, 0(4): 1-7.