PVC/PVDC共混膜的制备及其性能

doi:10.19398/j.att.202206032

摘要/Abstract

摘要： 为了探讨聚氯乙烯(PVC)/聚偏二氯乙烯(PVDC)共混膜的制备及性能,选用N,N-二甲基乙酰胺(DMAC)为溶剂,采用相转化法制备PVC/PVDC共混膜,研究PVC/PVDC共混体系的相容性、共混膜表面形貌和截面形貌,以及共混比和聚乙二醇(PEG)质量分数对纯水通量、截留率,动态接触角以及通量恢复率的影响。结果表明:当PVC/PVDC共混比为4/6时共混膜的综合性能最好,纯水通量为212.9 L/(m²·h),在0.1 MPa的压力下,对牛血清蛋白(BSA)的截留率为88.5%。PEG最佳质量分数为6%,此时纯水通量为336.6 L/(m²·h),截留率为81.6%,瞬间接触角从81.1°下降到74.5°,恢复通量率从52.7%上升到85.7%。研究结果说明PEG可以有效地改善共混膜的亲水性和抗蛋白污染能力。

关键词: 共混膜, 微观结构, 水通量, 亲水性, 抗污染性能

Abstract: Polyvinyl chloride (PVC) is one of the main membrane materials in modern times. It has excellent acid and alkali resistance, microbial resistance, high mechanical strength, low price and other advantages, and is widely used in ultrafiltration, nanofiltration and other fields. However, the film forming performance of PVC is not very ideal, the water flux is low, and the toughness is insufficient, so it is easy to shrink and wrinkle spontaneously when gel is used. Therefore, the PVC film needs to be modified by blending to improve its performance. Polyvinylidene chloride (PVDC) has good film forming property, good mechanical properties, thermal stability and chemical resistance. Therefore, blending PVC and PVDC can make the film have both advantages. In addition, due to the poor hydrophilicity of PVC and PVDC, polyethylene glycol (PEG) can be used as an additive to modify the blend membrane, which can improve its hydrophilicity, pollution resistance and pure water flux.
In order to investigate the preparation and properties of polyvinyl chloride(PVC)/poly(vinylidene chloride) (PVDC) blend membranes, N, N-Dimethylacetamide (DMAC) was used as solvent to prepare PVC/PVDC blend membranes by phase inversion method. The compatibility of PVC/PVDC blend system, the surface morphology and cross-sectional morphology of blend membranes, as well as the effects of blend ratio and polyethylene glycol (PEG) mass fraction on pure water flux, rejection, dynamic contact angle and flux recovery were studied. At present, a lot of studies on the blending modification of PVC membranes have been done at home and abroad, but the study on the modification of PVC membranes with PVDC has not been reported yet. The results show that when the blending ratio is 4/6, the overall performance of the blend membrane is the best, the pure water flux is 212.9 L/(m²·h), and the rejection rate of bovine serum albumin (BSA) is 88.5% under the pressure of 0.1 MPa. The optimum mass fraction of PEG is 6%, and at this time, the pure water flux is 336.6 L/(m²·h), the interception rate is 81.6%, the instantaneous contact angle decreases from 81.1° to 74.5°, and the recovery flux rate increases from 52.7% to 85.7%. The results show that PEG can effectively improve the hydrophilicity and anti-protein pollution ability of the blend membrane.
In this paper, PVC/PVDC blend membranes are prepared by phase inversion method. The compatibility of PVC/PVDC blend systems is analyzed and discussed by measuring the shear viscosity of solutions with different blend ratios. At the same time, the surface and section microstructures of PVC/PVDC blend membranes are observed by field emission scanning electron microscopy (SEM), and the contact angle, pure water flux and flux recovery rate and the interception rate of bovine serum albumin (BSA) are tested to determine the optimal blend ratio. On this basis, the influence of PEG mass fraction on the performance of the blend membrane is studied to determine the optimal PEG content, which provides some directions for the material selection and modification of PVC blend membranes, and endows them with a broader market prospect in water treatment and sewage treatment.

Key words: blend membrane, microstructure, water flux, hydrophilicity, anti pollution performance

中图分类号:

TQ028.8

周榆凯, 钱建华, 杨晶晶, 徐凯杨, 梅敏. PVC/PVDC共混膜的制备及其性能[J]. 现代纺织技术, 2023, 31(1): 145-152.

ZHOU Yukai, QIAN Jianhua, YANG Jingjing, XU Kaiyang, MEI Min. Preparation and properties of PVC/PVDC blend membranes[J]. Advanced Textile Technology, 2023, 31(1): 145-152.

参考文献

[1] FAN X, SU Y, ZHAO X, et al. Fabrication of polyvinyl chloride ultrafiltration membranes with stable antifouling property by exploring the pore formation and surface modification capabilities of polyvinyl formal[J]. Journal of Membrane Science, 2014, 464:100-109.
[2] JOMEKIAN A,MANSOORI S, MONIRIMANESH N. Synthesis and characterization of novel PEO-MCM-41/PVDC nanocomposite membrane-ScienceDirect[J]. Desalination, 2011, 276(1/ 2/ 3):239-245.
[3] 姚凯凯,邱广明,王海博,等.PVC/PVA共混膜的制备及性能研究[J].膜科学与技术,2019,39(3):36-40,69.
YAO Kaikai, QIU Guangming, WANG Haibo, et al. Preparation and performance characterization of PVC/PVA blend membranes[J]. Membrane Science and Technology, 2019, 39(3):36-40, 69.
[4] 蒋淑红,肖梦林,杨帆,等.PVC/PES-g-PEGMA共混膜的制备及其耐污染性能[J].环境工程学报,2015,9(5):2310-2316.
JIANG Shuhong, XIAO Menglin, YANG Fan, et al. Preparation and antifouling property of PVC/ PES-g-PEGMAblend membranes[J]. Journal of Environmental Engineering, 2015, 9(5):2310-2316.
[5] 程亮,王骥,龚旻,等.PVC-P(VC-VAC)-MBS共混超滤膜的制备及其性能[J].膜科学与技术,2016,36(3):8-12, 20.
CHEN Liang, WANG Ji, GONG Min, et al. Preparation and properties of PVC-P(VC-VAC)-MBS blend UF membranes[J]. Membrane Science and Technology, 2016, 36 (3):8-12, 20.
[6] 刘美惠,沈惠玲,王双双.碳纳米管对聚氨酯/聚氯乙烯共混膜性能的影响[J].塑料,2018,47(4):5-7,12.
LIU Meihui, SHEN Huiling, WANG Shuangshuang. Effects of carbon nanotubes on properties of polyurethane / polyvinyl chloride composite membranes[J]. Plastic, 2018,47(4):5-7, 12.
[7] 张大鹏,姜蕾,刘兆峰,等.MCM-48改性三醋酸纤维素正渗透膜的制备及性能表征[J].水处理技术,2017,43(3):25-28.
ZHANG Dapeng, JIANG Lei, LIU Zhaofeng, et al. Preparation and characterization of cellulose triacetate-based forward osmosis membrane modified with MCM-48 nanoparticles[J]. Water Treatment Technology, 2017, 43(3): 25-28.
[8] XU Y, LUO Y Y, WANG F, et al. Preparation and characterizations of poly(vinyl butyral)/caprolactam/polyethylene glycols hydrophilic flat-sheet membrane through thermally induced phase separation[J].Chemistry Select,2019,4(29):8500-8507.
[9] ZHOU Z, RAJABZADEH S, SHAIKH A R, et al. Effect of surface properties on antifouling performance of poly(vinyl chloride-co-poly(ethylene glycol)methyl ether methacrylate)/PVC blend membrane[J]. Journal of Membrane Science, 2016, 514:537-546.
[10] SHEN J N, YU C C, RUAN H M, et al. Preparation and characterization of thin-film nanocomposite membranes embedded with poly(methyl methacrylate) hydrophobic modified multiwalled carbon nanotubes by interfacial polymerization[J]. Journal of Membrane Science, 2013, 442:18-26.
[11] 杨波,肖通虎,迟莉娜.水-溶剂-PAN体系热力学和动力学对膜的影响[J].水处理技术,2019,45(12):76-80.
YANG Bo, XIAO Tonghu, CHI Lina. Effect of thermody-namics and kinetics of water/solvent/PAN ternary systems on membrane[J]. Water Treatment Technology, 2019, 45(12): 76-80.
[12] 陈欣,刘海亮,黄庆林,等.聚(偏二氯乙烯-氯乙烯)多孔膜制备及性能[J].高分子材料科学与工程,2017,33(8):171-177.
CHEN Xin, LIU Hailiang, HUANG Qinglin, et al. Preparation and properties of poly(vinylidene chloride-co-vinyl chloride) porous membrane[J]. Polymer Materials Science and Engineering, 2017,33(8):171-177.
[13] WANG S H, ZHANG X H, XI Z Y, et al. Design and preparation of polypropylene ultrafiltration membrane with ultrahigh flux for both water and oil[J].Separation and Purification Technology,2020,238: 116455.
[14] 刘倩文,张小娟,顾倩倩,等.添加剂PEG对CPVC/PVB共混膜性能的影响[J].化工进展,2017,36(4):1388-1394.
LIU Qianwen, ZHANG Xiaojuan, GU Qianqian, et al. Effects of additive PEG on the properties of CPVC/PVB blended membranes[J]. Progress in Chemical Industry, 2017,36(4):1388-1394.