侧基含磷阻燃共聚酯的熔融增黏反应特性分析

doi:10.19398/j.att.202203068

现代纺织技术 ›› 2022, Vol. 30 ›› Issue (6): 37-43.DOI: 10.19398/j.att.202203068

侧基含磷阻燃共聚酯的熔融增黏反应特性分析

尚小愉, 朱坚, 王滢, 张先明, 陈文兴

浙江理工大学材料科学与工程学院,杭州 310018

收稿日期:2022-03-29 出版日期:2022-11-10 网络出版日期:2022-11-16
通讯作者:张先明,E-mail:zhangxm@zstu.edu.cn
作者简介:尚小愉(1995—),女,河南濮阳人,硕士研究生,主要从事聚酯纤维材料方面的研究。
基金资助:
浙江省重点研发计划资助项目(2020C01143,2021C01020)

Melt polycondensation characteristics of flame retardant copolyesters containing phosphorus linked pendant groups

SHANGXiaoyu, ZHU Jian, WANG Ying, ZHANG Xianming, CHEN Wenxing

School of Materials Science & Engineering, Zhejiang Sci-Tech University, Hangzhou 310018, China

Received:2022-03-29 Published:2022-11-10 Online:2022-11-16

摘要/Abstract

摘要： 为研究侧基含磷阻燃共聚酯的熔融增黏反应,将侧基含磷阻燃剂共聚到聚对苯二甲酸乙二醇酯(PET)分子链中,制得侧基含磷阻燃共聚酯PET-D_x。对PET-D_x进行熔融缩聚增黏反应,分析不同反应因素(温度、时间、阻燃单体添加量)对增黏反应的影响。结果表明:PET-D_x的特性黏度随温度升高而逐渐增加,而在反应后期略微降低;阻燃单体中苯环结构产生的位阻效应对熔融增黏具有一定的抑制作用,故在270 ℃下,阻燃剂添加量为3%的PET-D₃增黏效果最好,反应2.5 h,特性黏度可达1.23 dL/g。最后,根据特性黏度的时间演变特性对熔融缩聚增黏的反应动力学进行研究,反应速率常数随温度的升高、阻燃单体添加量的减少而增加,而反应活化能却随阻燃单体添加量的增加而增加。

关键词: 侧基含磷阻燃剂, 共聚酯, 熔融增黏反应, 反应动力学

Abstract: In order to study the melt polycondensation of flame retardant copolyesters containing phosphorus linked pendant groups, the flame retardant containing phosphorus linked pendant groups was successfully introduced into the polyester molecular chain by direct esterification method. The experiment for copolyesters containing phosphorus linked pendant groups (PET-D_x) was carried out for melt polycondensation, and the influence of different reaction factors (temperature, time and the amount of flame retardant additive) on the polycondensation reaction was analyzed. The results showed that the intrinsic viscosity of PET-D_x gradually increases with the increase of temperatures, while the intrinsic viscosity of copolyester decreases slightly later in the reaction. The steric resistance effect generated by the benzene ring structure in the flame retardant monomer has a certain inhibitory effect on melt polycondensation, and at 270 ℃, PET-D₃ with an addition of 3% flame retardant has the best viscosity enhancement effect, the reaction lasts for 2.5 h, and the intrinsic viscosity can reach 1.23 dL/g. Finally, the reaction kinetics of melt polycondensation was studied according to the change of intrinsic viscosity with reaction time. The results show that the reaction rate constants of the polycondensation reaction increase with the increase of temperature and the decrease of flame retardant content, while the activation energies increase with the increase of flame retardant content.

Key words: flame retardant containing phosphorus linked pendant groups, copolyesters, melt polycondensation, reaction kinetics

中图分类号:

TQ342.92

尚小愉, 朱坚, 王滢, 张先明, 陈文兴. 侧基含磷阻燃共聚酯的熔融增黏反应特性分析[J]. 现代纺织技术, 2022, 30(6): 37-43.

SHANGXiaoyu, ZHU Jian, WANG Ying, ZHANG Xianming, CHEN Wenxing. Melt polycondensation characteristics of flame retardant copolyesters containing phosphorus linked pendant groups[J]. Advanced Textile Technology, 2022, 30(6): 37-43.

参考文献

[1] SONG Y, XUE B, WANG J, et al. Ammonium poly-phosphate wrapped carbon microspheres:A novel flame retardant with smoke suppression for poly (ethylene terephthalate)[J]. Journal of Polymer Research, 2020, 27(1): 1-12.
[2] SALAÜN F, LEMORT G, BUTSTRAEN C, et al. Influence of silica nanoparticles combined with zinc phosphinate on flame retardant properties of PET[J]. Advances in Polymer Technology, 2017, 28: 1919-1928.
[3] PENG Y, NIU M, QIN R H, et al. Study on flame retardancy and smoke suppression of PET by the synergy between Fe₂O₃ and new phosphorus-containing silicone flame retardant[J]. High Performance Polymers, 2020, 32(9): 1-12.
[4] FANG Y, LIU X, TAO X. Intumescent flame retardant and anti-dripping of PET fabrics through layer-by-layer assembly of chitosan and ammonium polyphosphate[J]. Progress in Organic Coatings, 2019, 134: 162-168.
[5] PHEM C T, NGUYEN B T, PHAN H T Q, et al. Highly efficient fire retardant behavior, thermal stability, and physicomechanical properties of rigid polyurethane foam based on recycled poly(ethylene terephthalate)[J]. Journal of Applied Polymer Science, 2020, 137(37): 49110.
[6] YAO Z Y, LIU X X, QIAN L J, et al. Synthesis and characterization of aluminum 2-carboxyethyl-phenyl-phosphinate and its flame-retardant application in polyester[J]. Polymers, 2019, 11(12): 1969.
[7] ZHANG Y, NI Y P, HE M X, et al. Phosphorus-containing copolyesters: The effect of ionic group and itsanalogous phosphorus heterocycles on their flame-retardant and anti-dripping performances[J]. Polymer, 2015, 60: 50-61.
[8] 袁效东,马建平,张先明,等.不同特性黏度PET切片的制备及加工特性研究[J].浙江理工大学学报(自然科学版),2017,37(2):208-213.
YUAN Xiaodong, MA Jianping, ZHANG Xianming, et al.Preparation of PET chips with various intrinsic viscosity and study on processing characteristics of PET chips[J]. Journal of Zhejiang Sci-Tech University (Natural Sciences Edition), 2017, 37(2): 208-213.
[9] 曹睿,陈锦国,李红华.PET聚酯切片特性黏度测试方法综述[J].合成技术及应用,2021,36(3):22-27.
CAO Rui, CHEN Jinguo, LI Honghua.Summary of viscosity test of polyester chips[J]. Synthetic Technology and Application, 2021, 36(3): 22-27.
[10] 马欣.聚酯固相缩聚进展综述及EcoSphere^TM新技术浅析[J].合成纤维,2019,48(6):4-12.
MA Xin. The progress review for ssp of pet and compre-hensive analysis for novel ecosphere process[J]. Synthetic Fiber in China, 2019, 48(6): 4-12.
[11] 姬洪,陈康,宋明根,等.阻燃共聚酯固相缩聚反应结晶动力学研究[J].东华大学学报(自然科学版),2021,47(1):1-6.
JI Hong, CHEN Kang, SONG Minggen, et al. Crystalliza-tion kinetics of flame retardant co-polyesters in solid state polymerization condensation[J]. Journal of Donghua University (Natural Science), 2021, 47(1): 1-6.
[12] LI L J, DUAN R T, ZHANG J B, et al. Phosphorus-containing poly(ethylene terephthalate): Solid-state polymerization and its sequential distribution[J]. Industrial & Engineering Chemistry Research, 2013, 52(15): 5326-5333.
[13] 万苏影,包建娜,王滢,等.含磷阻燃共聚酯的熔融增黏反应及其动力学[J].纺织学报,2021,42(11):9-16.
WAN Suying, BAO Jianna, WANG Ying, et al. Melt polycondensation and kinetics of phosphorus containing flame retardant copolyesters[J]. Journal of Textile Research, 2021, 42(11): 9-16.
[14] DUH B. Reaction kinetics for solid-state polymerization of poly(ethylene terephthalate)[J]. Journal of Applied Polymer Science, 2001, 81(7): 1748-1761.
[15] JI H, GAN Y, KUMI A K, et al. Kinetic study on the synergistic effect between molecular weight and phosphorus content of flame retardant copolyesters in solid-state polymerization[J]. Journal of Applied Polymer Science, 2020, 137(38): 49120.
[16] DUH B. Semiempirical rate equation for solid state polymerization of poly(ethylene terephthalate)[J]. Journal of Applied Polymer Science, 2002, 84(4): 857-870.
[17] KIM T Y, JABARIN S A. Solid-state polymerization of poly(ethylene terephthalate). III. Thermal stabilities in terms of the vinyl ester end group and acetaldehyde[J]. Journal of Applied Polymer Science, 2003, 89: 228-237.

侧基含磷阻燃共聚酯的熔融增黏反应特性分析

Melt polycondensation characteristics of flame retardant copolyesters containing phosphorus linked pendant groups

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 2

编辑推荐

Metrics

[1]	谢尚栋, 孙黎江, 朱开阳, 陈世昌, 陈文兴. Ti-Al双金属催化剂制备PEIT共聚酯及其热性能[J]. 现代纺织技术, 2022, 30(5): 89-96.
[2]	陈志薇, 张顺花. 呋喃基共聚酯PETT纤维的制备及其性能[J]. 现代纺织技术, 2022, 30(4): 102-107.