高长径比银纳米线的制备及其应用

doi:10.19398/j.att.20211028

现代纺织技术 ›› 2022, Vol. 30 ›› Issue (3): 65-72.DOI: 10.19398/j.att.20211028

高长径比银纳米线的制备及其应用

杨晶晶, 钱建华, 赵永芳, 彭慧敏, 梅敏

浙江理工大学纺织科学与工程学院,杭州 310018

收稿日期:2021-01-23 修回日期:2021-10-22 出版日期:2022-05-10 网络出版日期:2022-05-26
通讯作者:钱建华,E-mail:qianjianhua@zstu.edu.cn
作者简介:杨晶晶(1998-),女,浙江温州人,硕士研究生,主要从事新型纤维材料方面的研究。

Fabrication and application of high aspect ratio silver nanowires

YANG Jingjing, QIAN Jianhua, ZHAO Yongfang, PENG Huimin, MEI Min

College of Textile Science and Engineering, Zhejiang Sci-Tech University, Hangzhou 310018, China

Received:2021-01-23 Revised:2021-10-22 Published:2022-05-10 Online:2022-05-26

摘要/Abstract

摘要： 应用多元醇法制备银纳米线(AgNWs),分析影响银纳米线形貌的原因,并测试最佳条件下合成的AgNWs的外观形貌、化学结构、结晶性能,然后将AgNWs分散到无水乙醇中,对棉织物进行整理,最后采用浸渍-烘干法将AgNWs整理到已经过等离子体预处理的棉织物表面,对整理后的棉织物进行抗紫外性能、导电性、抗菌性能测试。结果表明:合成的最佳AgNWs最长可达127.54 μm,平均76.72 μm,长径比为1189;等离子体处理提高了棉织物对AgNWs的附着性能;AgNWs整理可使棉织物方块电阻低至5.67 Ω/sq,AgNWs质量浓度为10 g/L时,UPF值可达65.9,能够满足抗紫外标准,同时整理的棉织物能够形成明显的抑菌圈,具有抗菌效果。实验制备的棉织物具有多功能特性,可作为功能性织物进一步开发应用。

关键词: 银纳米线, 棉织物, 等离子体处理, 功能性

Abstract: Silver nanowires (AgNWs) were synthesized using polyol. The reasons affecting the morphology of silver nanowires were analyzed and the appearance, chemical structure and crystallization properties of AgNWs synthesized under the optimal conditions were tested. Then, AgNWs were dispersed into anhydrous ethanol to finish cotton fabric. Finally, AgNWs were finished on the surface of cotton fabric which had been pretreated by plasma by impregnation drying method, and the UV resistance, conductivity and antibacterial properties of the finished cotton fabric were tested. The results show that the longest length of AgNWs is 127.54 μ m, the average length is 76.72 μ m, and the ratio of length to diameter is 1189; the adhesion of AgNWs to cotton fabric is improved by plasma treatment; the sheet resistance of cotton fabric is as low as 5.67 Ω /sq, and when the mass concentration of AgNWs is 10 g/L, the UPF value can reach 65.9. At the same time, the finished cotton fabric can form an obvious antibacterial circle with antibacterial effect. The cotton fabric with multi-functional properties can be used as a functional fabric for further application.

Key words: silver nanowires, cotton fabric, plasma treatment, functionality

中图分类号:

TS156

杨晶晶, 钱建华, 赵永芳, 彭慧敏, 梅敏. 高长径比银纳米线的制备及其应用[J]. 现代纺织技术, 2022, 30(3): 65-72.

YANG Jingjing, QIAN Jianhua, ZHAO Yongfang, PENG Huimin, MEI Min. Fabrication and application of high aspect ratio silver nanowires[J]. Advanced Textile Technology, 2022, 30(3): 65-72.

参考文献

[1] SUN Y G, YIN Y D, MAYERS B T, et al. Uniform silver nanowires synthesis by reducing AgNO₃ with ethylene glycol in the presence of seeds and poly(vinyl pyrrolidone)[J]. Chemistry of Materials, 2002, 14(11): 4736-4745.
[2] 彭军,李津,李伟,等.银纳米线研究进展与应用[J].现代化工,2019,39(4):31-35.
PENG Jun, LI Jin, LI Wei, et al. Research progress and application of silver nanowires[J]. Modern Chemical Industry, 2019, 39(4): 31-35.
[3] 许杰,贾旺,李伟,等.银纳米线制备及应用研究进展[J].化工新型材料,2018,46(1):33-37.
XU Jie, JIA Wang, LI Wei, Research progress of silver nanowires preparation method and application[J]. New Chemical Materials, 2018, 46(1): 33-37.
[4] 丁晨,赵兵,祁宁.基于银纳米线导电网络的电子纺织品[J].化学进展,2017,29(8):892-901.
DING Chen, ZHAO Bing, QI Ning. Electronic textiles based on silver nanowire conductive network[J]. Progress in Chemistry, 2017, 29(8): 892-901.
[5] 陶国平.纳米材料在功能性纺织品上的应用与展望[J].棉纺织技术,2001,29(10):581-584.
TAO Guoping. Application and prospects of nanometer materials in functional textiles[J]. Cotton Textile Technology, 2001, 29(10): 581-584.
[6] MIA R, SULTANA S. Fabrication and properties of silver nanowires (AgNWs) functionalized fabric[J]. Applied Sciences.2020, 2(12): 1-15.
[7] LIAN Y, YU H, WANG M, et al. Ultrasensitive wearable pressure sensors based on silver nanowire-coated fabrics[J]. Nanoscale Research Letters, 2020, 15(1): 70.
[8] DOGANAY D, KANICIOGLU A, COSKUN S, et al. Silver-nanowire-modified fabrics for wide-spectrum antimicrobial applications(Article)[J]. Journal of Materials Research, 2019, 34(4): 500-509.
[9] KORTE K E,SKRABALAK S E,XIA Y N.Rapid synthesis of silver nanowires through a CuCl- or CuCl₂-mediated polyol process(Article)[J]. Journal of Materials Chemistry, 2008, 18(4): 437-441.
[10] WILEY B, SUN Y G, XIA Y N. Polyol synthesis of silver nanostructures: Control of product morphology with Fe(Ⅱ) or Fe(Ⅲ) species[J]. Langmuir, 2005, 21(18): 8077-8080.
[11] PRIYADARSHI R, NEGI Y S.Poly(vinyl pyrrolidone)-mediated synthesis of silver nanowires decorated with silver nanospheres and their antimicrobial activity[J]. Bulletin of Materials Science, 2019, 42(3): 1-7.
[12] CHEN S H, CARROLL D L. Synthesis and characteri-zation of truncated triangular silver nanoplates[J].Nano Letters, 2002, 2(9): 1003-1007.
[13] 闫腾,岳新霞,孙凤,等.高碘酸钠氧化对棉纤维基吸附剂吸附性能的影响[J].纺织导报,2014(2):84-87.
YAN Teng, YUE Xinxia, SUN Feng, et al. Effect of sodium periodate oxidation on adsorption properties of cotton fiber-based adsorbent[J]. China Textile Leader, 2014(2): 84-87.
[14] 朱虹烨,谢光银.低压等离子体改性棉织物表面性能研究[J].纺织科技进展,2020(7):20-22.
ZHU Hongye, XIE Guangyin. Surface modification of cotton fabrics by low pressure plasma[J]. Progress in Textile Science & Technology, 2020(7): 20-22.
[15] LAM Y L, KAN C W, YUEN C W M. Physical and chemical analysis of plasma-treated cotton fabric subjected to wrinkle-resistant finishing[J]. Cellulose, 2011, 18(2): 493-503.

高长径比银纳米线的制备及其应用

Fabrication and application of high aspect ratio silver nanowires

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

[1]	吴明星, 汪进前, 盖燕芳. 改性棉织物微/纳米拒水表面的构建及其性能[J]. 现代纺织技术, 2022, 30(5): 197-205.
[2]	谭卫, 马明波, 周文龙. 基于纳米Cs_0.33WO₃的自清洁多功能棉织物的制备及其性能[J]. 现代纺织技术, 2022, 30(5): 213-221.
[3]	陈春晖, 许多, 李治江, 吉强. 疏水亲油复合棉织物的制备及其性能[J]. 现代纺织技术, 2022, 30(4): 115-123.
[4]	于海娟, 杨斌, 傅红平, 余志成, 王磊. 菝葜根天然染料对改性棉织物的染色性能[J]. 现代纺织技术, 2022, 30(4): 156-161.
[5]	李慧慧, 王群, 贾伟科, 王际平. 多功能超疏水纺织品的制备及应用研究进展[J]. 现代纺织技术, 2022, 30(3): 39-46.
[6]	盛婷, 张佳文, 徐天祺, 胡叶蕾, 易玲敏. 基于纳米粒子改性短链含氟整理剂的棉织物拒水拒油整理[J]. 现代纺织技术, 2022, 30(2): 169-177.
[7]	李雪梅, 刘亚楠, 祝成炎, 金肖克, 王浙峰, 张红霞. 负载核壳结构维生素E纳米颗粒的粘胶纱交织物性能研究[J]. 现代纺织技术, 2022, 30(2): 127-133.
[8]	周梦云，阎玉秀，金子敏，陶建伟. 增生性瘢痕压力服研究与临床现状及展望[J]. 现代纺织技术, 2021, 0(5): 78-87.
[9]	张淑军,李刚,张鸿,张明其,刘燕平,潘志娟. 阳离子染料可染改性涤纶及其面料的研究进展[J]. 现代纺织技术, 2021, 0(4): 115-120.
[10]	杨丹,刘丽妍,李婷,韩永良,白静娜. 低温等离子体预处理针织管增强PVDF中空纤维膜性能分析[J]. 现代纺织技术, 2021, 0(3): 16-22.
[11]	李朝利，汪进前，盖燕芳，邓成浩，朱贤敏. 银复合棉织物的制备及导电性能研究[J]. 现代纺织技术, 2021, 0(1): 41-46.
[12]	梁晓颖，王利君. 棉织物柿漆染色工艺及性能[J]. 现代纺织技术, 2021, 0(1): 68-75.
[13]	陈梦颖，陈慰来，沈建春，岑柳莎. 除甲醛功能窗帘的特性研究及开发[J]. 现代纺织技术, 2020, 0(6): 24-29.
[14]	章水龙，陈顺明，程四新，章友鹤. 新型纱线的开发与研究——对浙江省纺纱企业开发新型纱线、拓展应用领域情况的研究分析[J]. 现代纺织技术, 2020, 0(4): 25-32.
[15]	申美丽，徐伯俊，刘新金，苏旭中，曹秀明. 纱线捻度对纯棉机织物保形性能的影响研究[J]. 现代纺织技术, 2019, 0(06): 47-51.